Delivery within 12 to 18 hours
Fast, dependable delivery helps keep projects on schedule by ensuring cement reaches site when it is needed.
Higher strength. Smarter economics
MAXLOAD Bulk Cement is a high-strength Ordinary Portland Cement (OPC-53) manufactured from 96% high-purity limestone and built for large-scale construction where consistent quality and uninterrupted supply are non-negotiable.
Best for
Large-scale infrastructure
Industrial construction
Ready-mix concrete plants
Large residential and commercial projects
Pre-stressed and post-tensioned structures
Why experts choose MAXLOAD Bulk Cement
96% high-purity limestone
MAXLOAD Bulk Cement is manufactured from 96% high-purity limestone, a raw material quality that directly contributes to its superior strength and consistency across every batch.
20% higher 28-day strength
MAXLOAD Bulk Cement achieves 20% higher compressive strength at 28 days compared to the minimum BIS requirement, delivering structures that are stronger and more durable over their lifetime.
30% higher 3-day strength
Significantly higher early strength means faster formwork removal, faster floor cycles and a measurable reduction in overall construction time on large-scale projects.
Low chlorides, sulphur and alkalis
Tightly controlled chemical composition minimises the risk of reinforcement corrosion, sulphate attack and alkali-silica reaction, protecting structural integrity over the long term.
25% higher-than-norm fineness
Finer grinding means better particle distribution, improved reactivity and more consistent strength development, batch after batch, project after project.
10X lower Le Chatelier expansion
Soundness that is ten times better than the BIS minimum means MAXLOAD Bulk Cement will not expand excessively after setting, eliminating a key risk factor for cracking in large structural pours.
50% lower LOI (Loss on Ignition)
Every batch of MAXLOAD Bulk Cement is delivered with 50% lower Loss on Ignition than the BIS norm, a direct indicator of cement freshness and raw material quality at the point of use.
(All values and percentages are compared against minimum specified BIS requirements.)
Technical Specifications
PHYSICAL PROPERTIES
Parameter | What this measures | IS 269:2015 requirementt | Priya Cement |
|---|---|---|---|
Fineness — specific surface | How finely the cement is ground. Higher fineness means better reactivity and strength development. | Min. 225 m²/kg | 288 m²/kg |
Initial setting time | How long the cement remains workable after mixing with water. | Min. 30 minutes | 140 minutes |
Final setting time | How long before the cement becomes fully rigid and cannot be disturbed. | Max. 600 minutes | 220 minutes |
Le Chatelier expansion | Measures soundness, whether the cement expands excessively after setting, which can cause cracking. | Max. 10.0 mm | 1.0 mm |
Autoclave expansion | A more stringent test of soundness under high pressure and temperature. | Max. 0.8% | 0.067% |
COMPRESSIVE STRENGTH
Curing period | IS 269:2015 minimum | Priya Cement test result |
|---|---|---|
3 days | Min. 27 MPa | 36 MPa |
7 days | Min. 37 MPa | 45 MPa |
28 days | Min. 53 MPa | 66 MPa |
Chemical properties
Parameter | What this measures | IS 269:2015 | Priya Cement |
|---|---|---|---|
Loss on ignition | Measures the proportion of material lost when heated, an indicator of cement freshness and quality. | Max. 4.0% | 2.04% |
Insoluble residue | Measures impurities that do not dissolve in acid, lower values indicate higher purity. | Max. 5.0% | 4.04% |
Sulphuric anhydride | Controls sulphate content, which affects setting time and long-term durability. | Max. 3.5% | 1.77% |